LTPZW-3600 serials
Author:admin  From:Letian Plastics  Hits:2081  Update:2008-12-9

Resin of LTP ZW-3600 serials is crystal whisker reinforced composite materials based on high molecular weight linear PPS and PEEK alloy. With the characteristics of excellent high strength, rigidity, wear-resisting, heat-resisting, chemical-resisting and outstanding mold technology, the materials can meet the needs of product to replace copper alloy and hard alloy for varied fields.

Mechanics of machinery data for LTP ZW-3600 serials engineering plastic

Item

Unit

Test method

ZW-3100
ZW-3125
ZW-3150
Tensile strength
Mpa
GB/T1040
80
100
125
Rate of elongation
%
GB/T1040
0.3
0.5
0.6
Flexural strength
Mpa
GB1042
150
160
180
Impact strength (notched)
KJ/M2
GB/T1043
5.0
6.0
6.0
Compression strength8894.com
Mpa
GB1041
235
260
290
Rigidity
HRA
GB/T9342
65
75
80

Temperature of thermal
deformation

GB1634
>265
Chemical resistance
   
Thermal retardance2998.com
 
UL94
V-0
Abrasion value
10Mpa/24h
老葡京
μm
乐天法
1.0
Coefficient of kinetic friction
S
GB/T3960
0.02
PV value
 
 
1600
2000
2250
Melt flow rate新葡京官方网址
g/10min
GB3682
15—30
Coefficient of thermal expansion
Flow direction
Vertical direction
×10-5/℃
GB/T2572
—2.0
—3.5
Mold shrinkage rate
Flow directional
Vertical direcational
m/m
80×80×3
<0.001
<0.002
Density
Kg/m3
GB1033
1.65
Water absorption
%
GB1034
0.2-0.3
Colour
 
Visual method
Colour matching as requirement of customer
Copyright:Chengdu Letian Plastics Co.,Ltd Technical: 
Add:Gaopeng Chengdu Road on the 8th (high-tech zones) Post:610041
Tel:028-85182892 028-85132168 Fax:028-85161483 Website:www.cnletian.com Email:sggl@cnletian.com